低温陶瓷、玻璃熔剂组成列表
(特别声明：鉴于技术保密原因，本网站所提供化学组成，和实际产品会有一定差别，仅供参考,使用中以您所得到的商品为准。）
|
编号 |
SiO2 |
Al2O3 |
CaO |
MgO |
K2O |
Na2O |
PbO |
B2O3 |
线膨胀系数 |
|
RF-3005 |
10.87% |
0.00% |
0.00% |
0.00% |
0.00% |
8.21% |
68.94% |
11.98% |
9.68E-06 |
|
RF-3012 |
32.52% |
2.55% |
0.00% |
0.00% |
0.00% |
0.00% |
64.93% |
0.00% |
6.69E-06 |
|
RF-3017 |
19.95% |
0.00% |
0.00% |
0.00% |
0.00% |
6.40% |
59.27% |
14.38% |
8.56E-06 |
|
RF-3044 |
28.10% |
2.30% |
0.10% |
0.00% |
1.40% |
0.30% |
67.80% |
0.00% |
7.35E-06 |
|
RF-3052 |
35.60% |
0.00% |
0.00% |
0.00% |
0.00% |
6.10% |
44.50% |
13.80% |
7.75E-06 |
|
RF-3054 |
28.09% |
0.00% |
5.50% |
0.00% |
0.00% |
0.00% |
66.40% |
0.00% |
7.31E-06 |
|
RF-3059 |
32.20% |
2.50% |
0.00% |
0.00% |
0.00% |
0.00% |
65.30% |
0.00% |
6.70E-06 |
|
RF-3124 |
0.00% |
0.00% |
42.09% |
0.00% |
0.00% |
0.00% |
0.00% |
57.91% |
8.02E-06 |
|
RF-3137 |
28.10% |
2.30% |
0.10% |
0.00% |
1.40% |
0.30% |
67.80% |
0.00% |
7.35E-06 |
|
RF-3139 |
19.90% |
0.00% |
0.00% |
0.00% |
0.00% |
6.40% |
59.20% |
14.50% |
8.56E-06 |
|
RF-3147 |
16.90% |
0.00% |
0.00% |
0.00% |
0.00% |
0.00% |
63.30% |
19.80% |
6.46E-06 |
|
RF-3170 |
40.50% |
4.00% |
0.00% |
0.00% |
0.00% |
1.10% |
54.40% |
0.00% |
6.61E-06 |
|
RF-3173 |
26.80% |
0.00% |
5.60% |
0.00% |
0.00% |
0.00% |
67.60% |
0.00% |
7.38E-06 |
|
RF-3196 |
40.50% |
4.80% |
0.00% |
0.00% |
0.00% |
2.10% |
52.60% |
0.00% |
6.91E-06 |